17-4PH stainless steel H1075 is a precipitation-hardened martensitic stainless steel (17% Cr, 4% Ni, Cu, Nb) heat-treated to the H1075 condition, providing high strength (typically 1310 MPa yield) with moderate corrosion resistance suitable for aerospace fasteners, pump shafts, and turbine components operating to ~300°C. The H1075 temper offers a balance of tensile strength and fracture toughness through controlled precipitation hardening, with applications spanning military and commercial aircraft engines and hydraulic systems per AMS 5604/5643 specifications.
Compliance & Regulations
1 interactive curve for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Compressive Modulus(Ec) | Curve (10 pts) | Pa | — | ||
Elongation at Break(εf)3 entries | 13.00 | - | 22°C · Forging/Tubing · H1075 · AMS 5643 · L · t=<8.000 in | ||
| ↳ | 13.00 | - | 22°C · Bar · H1075 · AMS 5643 · L · t=<8.000 in | ||
| ↳ | 14.00 | - | 22°C · Bar · H1075 · AMS 5643 · L · t=<8.000 in | ||
Poisson's Ratio(ν) | 0.2700 | - | 22°C | ||
Shear Modulus(G) | 87.56 | GPa | 22°C · Investment Casting | ||
Ultimate Tensile Strength(σUTS) | 0.9653 – 1.034 | GPa | 5 entriesClick to expand | ||
Yield Strength (0.2% offset)(σy) | 792.9 – 986.0 | MPa | 5 entriesClick to expand | ||
Young's Modulus(E) | 196.5 | GPa | 22°C · Sheet/Strip/Plate | ||
3 interactive curves for this material
Stress-strain, S-N fatigue and environmental knockdown curves are free with an account.
Create free account| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
CTE vs Temperature(α(T)) | Curve (13 pts) | 1/K | — | ||
Specific Heat vs Temperature(Cp(T)) | Curve (17 pts) | J/(kg·K) | — | ||
Thermal Conductivity vs Temperature(k(T)) | Curve (17 pts) | W/(m·K) | — |
| Property | Value | Unit | Conditions | Source | |
|---|---|---|---|---|---|
Density(ρ) | 7.806 | kg/m³ | 22°C |